Hybrid contact lens system and method

ABSTRACT

Methods of manufacturing hybrid contact lenses using a mold are provided. The methods include pouring liquefied resin of a substantially rigid material within an inner section, curing the substantially rigid material, pouring liquefied resin of a substantially flexible material within an outer section and curing the substantially flexible material. In some embodiments, a wall disposed between the rigid and flexible materials is angled and/or bent to increase bonding strength between the rigid and flexible sections. The curing steps involve the application of heat, UV light, or a combination of both heat and UV light.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of U.S. patent application Ser. No. 10/657,061, filed Sep. 5, 2003, which claims priority to U.S. Provisional Application Ser. No. 60/408,618, filed Sep. 6, 2002, the contents of which are incorporated herein by reference in their entirety.

FIELD OF THE INVENTION

The present invention generally relates to contact lenses, and more particularly to hybrid hard-soft contact lenses.

BACKGROUND OF THE INVENTION

Vision correction is on the verge of a revolution. New technologies to measure the aberrations or distortions in the optics of the eye will soon be available to the public. These new wavefront measurement techniques such as Shack-Hartmann wavefront sensing or Talbot Interferometry can precisely measure the eye's aberrations so that vision may be corrected up to 20/10. Wavefront sensing is the method for rapidly, and very accurately, assessing the aberrations in an individual's eye to create a customized prescription for correction.

However, once the eye's aberrations have been measured, either by conventional methods or by wavefront sensing, these measurements must then be transferred into a vision correction system, such as eye surgery, spectacles, or contact lenses. Recent advances in laser refractive surgery techniques such as LASIK and photorefractive keratectomy, as well as improvements in spectacle lens manufacturing now enable the creation of highly accurate corrective prescriptions for individuals.

However, this is not the case with contact lenses. Popular soft contact lenses cannot achieve the same result as spectacles or laser refractive surgery because of dimensional variations in fabrication. Hard contact lenses, which may provide the platform to achieve the results of spectacles, are not as comfortable as soft contacts and lack the necessary positional stability on the eye.

Therefore, there exists a need for a hybrid hard-soft contact lens that can provide a platform for a corrective prescription and also provide the comfort of soft contact lenses.

One drawback associate with hybrid hard-soft contact lens concerns a lack of sufficient bonding between hard and soft sections. This lack of bonding strength may result in debonding of the soft and hard sections at the bonding junctions after short periods of use.

Therefore, there exists a need for methods of manufacturing a hybrid hard-soft contact lens that produces sufficient bonding between hard and soft sections to prevent tearing of the lens at the bonding junctions.

SUMMARY OF THE INVENTION

A hybrid hard-soft contact lens is provided. Several embodiments of the invention include methods of coupling the hard section of the lens to the soft section of the lens. Other embodiments of the invention include contact lens materials that increase oxygen transmission though the lens. Yet other embodiments of the invention are directed to cost-effective manufacturing methods of a hybrid hard-soft contact lens.

The present invention also provides methods of using base curve molding to produce hybrid hard-soft contact lens that includes sufficient bonding between hard and soft sections to prevent tearing of the lens at the bonding junctions. Some embodiments include methods of coupling the hard section of the lens to the soft section of the lens, while other embodiments include cost-effective manufacturing methods of a hybrid hard-soft contact lens.

Further embodiments concern the manufacturing of a two-material button starting from a casting. Other embodiments concern the manufacturing of a two-material button using a preform base curve molding. Advantageously, the preform base curve molding obviates an expensive base curve lathing operation and only requires front surface lathing to manufacturing a stock or custom hybrid lens.

One aspect of the present invention involves a method of manufacturing a hybrid contact lens using a mold including an inner section and an outer section that are separated by an inner wall. The method includes the steps of pouring liquefied resin of a substantially rigid material within the inner section, curing the substantially rigid material, pouring liquefied resin of a substantially flexible material within the outer section and curing the substantially flexible material. The inner wall may be angled and/or bent to increase bonding strength between the rigid and flexible sections. The curing steps involve the application of heat, UV light, or a combination of both heat and ultraviolet (UV) light. A UV blocking material such as 4-methacryloxy-2-hydroxybenzophenone can also be incorporated in the formulation to absorb the UV light and to prevent cataract development.

In a preferred embodiment, the inner wall comprises a pre-form optical grade divider that divides the substantially rigid material and the substantially flexible material. In additional, the inner wall preferably is bondable with the substantially rigid material and the substantially flexible material. According to some embodiments, the method further includes the steps of coating the inner wall with a UV curable adhesive to promote bonding with the substantially rigid material and the substantially flexible material and removing the outer wall after the step of curing the substantially flexible material.

Another aspect of the present invention involves a method of manufacturing a hybrid contact lens using a block mold having a central void. The method includes the steps of pouring liquefied resin of a substantially rigid material within the central void, curing the substantially rigid material, removing the substantially rigid material from the block mold, attaching a guard to the substantially rigid material, pouring a predetermined amount of liquefied resin of flexible material into an area between the substantially rigid section and the guard and curing the substantially flexible material. The central void defines an inner wall that forms the shape of the junction between the substantially rigid material and the substantially material. This wall may be angled and/or bent to increase bonding strength between the rigid and flexible sections. The curing steps involve the application of heat, UV light, or a combination of both heat and UV light. The central void can also be molded using less expensive materials for the non-optical areas.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a front view of a manufacturing step used to construct a hybrid hard-soft contact lens of the present invention;

FIG. 2. is a front view of a contact lens blank after the manufacturing step illustrated in FIG. 1;

FIG. 3 is a front: view of another manufacturing step used to construct a hybrid hard-soft contact lens of the present invention;

FIG. 4 illustrates another manufacturing step used to construct a hybrid hard-soft contact lens of the present invention;

FIG. 5 illustrates an alternative manufacturing method of constructing a hybrid hard-soft contact lens of the present invention;

FIG. 6 illustrates several embodiments of interface geometries between a hard section and soft section of a hybrid hard-soft contact lens constructed according to the present invention;

FIG. 6A illustrates a preferred embodiment of an interface geometry between a hard section and soft section of a hybrid hard-soft contact lens constructed according to the present invention;

FIG. 7 is an illustration of a contact lens, several eye components and visible light rays exiting the eye-contact lens system;

FIG. 8 is another illustration of a contact lens, eye components and visible light rays, showing the tendency for different colored light rays to exit the eye at different angles;

FIG. 9 illustrates a hypothetical uniform eye response to the visible light spectrum;

FIG. 10 illustrates a photopic eye response to the visible light spectrum; and

FIG. 11 illustrates one idealized net wavelength response for a contact lens constructed according to the present invention.

FIG. 12 is a cross-sectional view of a hybrid contact lens mold according to the principles of the present invention;

FIGS. 13A-13D are cross-sectional views of the hybrid contact lens molds of FIG. 12, wherein each view includes an alternative inner wall;

FIG. 14 is a cross-sectional view of the hybrid contact lens mold of FIG. 12 after the inner section has been filled with a substantially rigid polymer and cured;

FIG. 15 is a cross-sectional view of the hybrid contact lens mold of FIG. 14 after the outer section has been filled with a substantially flexible polymer and cured;

FIG. 16 is a cross-sectional view of an alternative hybrid contact lens mold according to the principles of the present invention;

FIGS. 17A-17D are cross-sectional views of the hybrid contact lens molds of FIG. 16, wherein each view includes an alternative junction shape;

FIG. 18 is a cross-sectional view of the hybrid contact lens mold of FIG. 16 after the central void is filled with a substantially rigid polymer and cured;

FIG. 19 is a cross-sectional view of the hybrid contact lens mold of FIG. 18 after separation of the mold;

FIG. 20 is a cross-sectional view of the hybrid contact lens mold of FIG. 19 after the addition of a guard;

FIG. 21 is a cross-sectional view of the hybrid contact lens mold of FIG. 20 after the substantially flexible polymer is poured and cured;

FIG. 22 is a cross-sectional view of a further alternative hybrid contact lens mold according to the principles of the present invention;

FIG. 23 is a cross-sectional view of the hybrid contact lens mold of FIG. 22 after the inner section has been filled with a substantially rigid polymer and cured;

FIG. 24 is a cross-sectional view of the hybrid contact lens mold of FIG. 23 after the outer has been filled with a substantially flexible polymer and cured;

FIG. 25 is a cross-sectional view of another alternative hybrid contact lens mold according to the principles of the present invention;

FIG. 26 is a cross-sectional view of the hybrid contact lens mold of FIG. 25 after the central void has been filled with a substantially rigid polymer and cured;

FIG. 27 is a cross-sectional view of the hybrid contact lens mold of FIG. 26 after separation of the mold;

FIG. 28 is a cross-sectional view of the hybrid contact lens mold of FIG. 27 after the addition of a guard;

FIG. 29 is a cross-sectional view of the hybrid contact lens mold of FIG. 28 after the substantially flexible polymer is poured and cured;

FIG. 30 is a cross-sectional view of a pre-formed substantially rigid center portion suitable for use with the pre-shape mold of FIGS. 31-33;

FIG. 31 is a cross-sectional view of yet another alternative hybrid contact lens mold according to the principles of the present invention;

FIG. 32 is a cross-sectional view of the hybrid contact lens mold of FIG. 31 after the outer portion of the bowl-shaped void has been filled with a substantially flexible polymer and cured; and

FIG. 33 is a cross-sectional view of the hybrid contact lens mold of FIG. 32 after separation of the mold.

It will be recognized that some or all of the Figures are schematic representations for purposes of illustration and do not necessarily depict the actual relative sizes or locations of the elements shown.

DETAILED DESCRIPTION OF THE INVENTION

In the following paragraphs, the present invention will be described in detail by way of example with reference to the attached drawings. Throughout this description, the preferred embodiment and examples shown should be considered as exemplars, rather than as limitations on the present invention. As used herein, the “present invention” refers to any one of the embodiments of the invention described herein, and any equivalents. Furthermore, reference to various feature(s) of the “present invention” throughout this document does not mean that all claimed embodiments or methods must include the referenced feature(s).

The present invention is based on a hybrid contact lens platform that offers the benefits, without the disadvantages, of both soft and gas permeable contact lenses—comfort, health, stability, superior optics and durability. The features of the present invention include lens chemistry, manufacturing processes, optical design and prescribing and fitting processes. One feature of the manufacturing processes and optical design elements is the ability to make quarter wavelength customization in order to correct for the higher order refractive aberrations that limit one's ability to see better than 20/20.

Unless defined otherwise, all technical and scientific terms used herein have the same meaning as is commonly understood by one of skill in the art to which this invention belongs. In event the definition herein is not consistent with definitions elsewhere, the definitions set forth herein will control. As used herein, “hybrid” refers to a type of contact lens that includes both hard and soft lens elements.

One embodiment of the present invention will correct normal ametropic errors (myopia, hyperopia and astigmatism) to a higher degree of visual performance than conventional contact lenses. Another embodiment of the present invention will correct for the wavefront-guided higher order aberrations and will create a new contact lens category, providing “super vision” for those whose visual requirements demand better than 20/20 acuity. Yet another embodiment of the present invention will correct for presbyopia, the gradually increasing inability to focus at close distances that usually begins after age 40. Other embodiments of the present invention may include contact lenses that incorporate several, or all of the above-described features.

Another embodiment of the present invention is a hybrid lens that combines the optical clarity, stability and durability of a gas permeable lens with the comfort of a soft contact lens. This hybrid lens has a hard gas permeable center chemically bonded to a soft outer skirt. The center is highly oxygen permeable, which is important to maintaining corneal health. One of the manufacturing processes of the present invention enables this gas permeable center to be lathed to quarter wavelength precision, allowing corrections of wavefront-guided higher order refractive aberrations and providing visual performance better than 20/20.

Yet another embodiment hybrid contact lens of the present invention has a soft outer skirt with a radius of curvature greater than the base curve of the oxygen permeable center, which is suspended on the soft skirt, thus creating a lighter touch above the corneal apex. One feature of this embodiment is that the eyelid force of normal blinking creates a peristaltic-like pump that exchanges the tears under the lens, contributing to overall comfort, and eliminating dryness, the most frequent complaint of contact lens wearers. Another feature of this embodiment is that the tear layer under the lens is not only important for comfort and health, but it has optical correction qualities as well. A layer of tears retained behind the base curve of the gas permeable lens of the present invention may correct corneal astigmatism by up to about ten diopters. Thus, a hybrid contact lens constructed according to the present invention creates a superior astigmatism correcting capability that does not rely on orientation and positioning, as do soft contact lenses.

Another embodiment of the present invention comprises a hybrid lens with a substantially rigid center that is chemically bonded to a softer outer skirt. One embodiment of the outer skirt is comprised of a modified poly(2-hydroxyethyl methacrylate) HEMA (poly-2-hydroxyethyl-methacrylate) material. The center is a substantially rigid gas permeable-type with a gas permeability DK value greater than 30. A preferred embodiment center would have a gas permeability DK value of about 150. However, other embodiments may have a gas permeability DK value that may range between about 30 to about 250. In a preferred embodiment of the present invention, the substantially rigid center is made from any of the following materials: fluoro-siloxane acrylate, siloxane acrylate, or poly-stryene siloxane acrylate.

The substantially rigid center section may have a thickness that may range between about 0.03 millimeters (mm) to about 0.5 mm., and a diameter that may range between about 4.0 mm. to about 12.0 mm. The overall diameter of a hybrid contact lens constructed according to the present invention may range between about 10.0 nm. to about 18.0 mm.

The substantially rigid center may have a spherical or ellipsoidal ocular (i.e., eye-facing) surface. Unlike soft lenses, the substantially rigid center of the present invention contact lens is resistant to protein deposition. One feature of the present invention contact lens is that it is also highly resistant to foreign body migration as well as dislodgement from the eye during contact sports, or other vigorous activities. A contact lens constructed according to the present invention also provides excellent centering and vision correction for irregular corneas created by trauma or surgery.

Hybrid Contact Lens Geometry

One embodiment of the present invention comprises a central substantially rigid gas permeable portion having a posterior surface that is either spherical, aspherical or toroidal, which is chosen to approximate the overall toricity and sagittal depth of the cornea to be fitted. The rigid gas permeable portion may be optically clear with only the reduction in light transmission normally found in similar polymerized materials. In one embodiment the rigid portion contains colorants and additives that narrow the band of light transmitted by the lens to reduce the chromatic aberration of the lens-eye system. The anterior or posterior surface of the rigid portion may also have surface modification to correct the total low and high order aberrations of the lens-eye system. Further, the surface profile of the anterior or posterior surface may be modified to register the low and high order aberrations over the optical system of the eye to account for the consistent natural displacement of the contact lens when applied to the eye. In addition, the surface profile of the anterior or posterior surface may be modified to contain a multi-focal feature for the correction of presbyopia. Also, the anterior surface of the lens may be treated to reduce the variance in the pre-lens tear film.

In another embodiment of the present invention, the substantially rigid contact lens portion is joined to an outer soft hydrophilic portion by an intermediate adhesion enhancement zone. The adhesion enhancement zone may contain a material that bonds to the substantially rigid portion and to the soft hydrophilic portion. The soft hydrophilic portion may have a posterior surface that is spherical, aspherical, toroidal or rotationally asymmetrical to approximate the overall or meridional sagittal depth of the peripheral cornea, limbal region and sclera. The anterior surface of the soft portion may be modified to produce a thickness variation in the form of prism ballast or thin zones that utilize lid interaction to produce a resultant rotational stability.

The soft section or skirt of the contact lens is designed to control rotation by various methods. The methods include prism ballasting, thin zones, and rotationally asymmetrical contours that match the asymmetry of the cornea, limbus and sclera. In the preferred embodiment the superior portion of the lens is thinner than the inferior portion.

Methods of Manufacturing a Hybrid Contact Lens

Referring to FIGS. 1-5, one method of manufacturing a hybrid contact lens according to the present invention will now be described. This method results in a fracture resistant product that is inexpensive to manufacture.

Shown in FIG. 1, a rod 10 of rigid gas permeable material is cast having the desired characteristics. Upon the completion of the curing the rod is precision ground to produce a substantially uniform diameter. The rod is then machined by tool 15 into a primary blank 17 having an anterior diameter 20 designed to conform to the collet of a computer numerically controlled lathe and a posterior diameter 25 designed to conform the outermost diameter of the hydrophilic portion of the lens for positioning in a tube, cup, or other containing device. The anterior diameter 20 may range from 6 millimeters (mm) to 24 mm, and the posterior diameter 25 may range from 6 mm to 24 mm. In one embodiment, the anterior diameter 20 may be a separate material that is bonded or otherwise attached to the primary blank 17 for enduring the clamping force of a lathe. The intermediate portion of the primary blank 17 is simultaneously machined to have a predetermined angle 30 for the interface of the rigid and hydrophilic material in the finished lens.

One manufacturing method of the present invention has the posterior diameter 25 substantially meet, or exceed, the hydrophilic section outermost diameter 35, that is, the outermost diameter of the soft section of the contact lens, as shown in FIG. 4. In this embodiment, a boundary material 40 is then applied to produce a resultant wall, or cup to receive, and retain the hydrophilic liquid polymer. Alternatively, the primary blank 17 may be inserted into a cup, tube or other containing device to receive the hydrophilic material.

An alternative manufacturing method of the present invention includes the application of an adhesion promoter to the primary blank 17, followed by the casting of the hydrophilic polymer into the liquid holding device formed by either the boundary material 40, tube, cup or other containing device.

In yet another embodiment, the primary lens blank 17 is mounted via the anterior diameter 20 in the collet of a computer numerically controlled lathe that is programmed to produce the aspherical posterior surface profile in a manner that the profile does not require polishing, or may only need a light buff, or polish. The posterior surfaced button is then mounted to a lens block wherein the axis of the block passes through the geometric center of the lens 45, shown in FIG. 4.

The assembly with the posterior surfaced button is remounted in the collet of a computer numerically controlled lathe, such as the Optoform 80 with Variform attachment, or equivalent type that is capable of producing rotationally symmetrical or non-symmetrical surfaces to high, or quarter wavelength accuracy that preferably require a light buff, or no supplemental polishing (VARIFORM and OPTOFORM are trademarks of Precitech, Inc., of Keene, N.H.). It Will be appreciated to those skilled in the art that other types of lathes may be employed. The finished lens is then removed from the lathe, with or without a light buff, deblocked and cleaned followed by anterior lens surface treatment. Finally the lens undergoes hydration-extraction, sterilization and packaging.

Alternative manufacturing methods of the present invention may include: molding of the posterior surface and diamond turning of the molded blank; contour cutting of the anterior surface of a posterior curve finished blank; etching the anterior surface of a posterior curve finished blank or predicate lens anterior or posterior surface; thin film deposition of a predicate lens anterior or posterior surface; and laser ablation of a predicate lens anterior or posterior surface.

Another manufacturing method may include molding or lathing a standard base curve with a standard or semi-customized front surface, then using a thermal or laser energy to modify the refractive index of the center material to a desired optical requirement. This method replaces custom lathing or molding expenses. Another method may include molding the posterior and anterior surfaces, and yet another embodiment may include a mechanical force or thermal molding manufacturing method.

Another method of manufacturing a hybrid contact lens according to the present invention is illustrated in FIG. 5. Step 1 shows a rod of fluorosiloxane acrylate RGP material that will comprise the substantially rigid section of the hybrid contact lens. It will be appreciated to those skilled in the art that other types of materials may be employed. These other materials may include the following monomers, monomer mixtures, or their derivatives: methyl methacrylate; ethyl methacrylate; ethylene glycol diacrylate; octafluoro pentyl methacrylate, tetramethyldisiloxane, ethylene glycol dimethacrylate, pentafluoro phenylacrylate, 2-(trimethylsiloxyl)ethyl methacrylate, 2,2-bis(2-metharyloxyphenyl) propane, N-[2-(N,N-dimethylamino)ethyl] acrylate, 2-(N,N-dimethylamino)ethyl methacryalte, 2-(N,N-dimethylamino)propy acrylate, N-vinyl-2-pyrrolidone, N,N-dimthylacrylamide, acrylamide, acrylamine, 2-hydroxyethyl methacrylate, siloxane-ethylene glycol dimethacrylate, trifluoroethyl methacrylate, pentafluorostyrene, pentafluorophenyl methacrylate, pentafluorophenyl acrylate, pentafluoropropyl methacrylate, unsaturated polyester; p-vinyl benzylhexafluoroisopropyl ether, and siloxanylalkylamide.

The rod, or button shown in Step 1 of FIG. 5, will preferably have a 5 millimeter (mm) to 22 mm diameter and be 2 mm to 15 mm in length. In one embodiment, the button may be bonded to another material for a subsequent operation, and as a possible cost saving. In Step 2, a plunge tool is used to remove unnecessary hard material and allow a solid section of material on one side for subsequent operations. Another method may use the plunge tool to form the button assembly from Step 1, with a shape similar to FIG. 2.

In Step 3, a spacer is formed on the gripping side of the blank for the next operation, or the blank can be bonded to a pre-form containing device to skip Step 4.

In Step 4, a tape, or other media that provides a retaining wall to hold the soft material during polymerization is applied to the blank. In Step 5, an adhesion promoter may be applied to the hard material and then the soft material is poured inside the retaining wall, or other containing device, and allowed to cure. In Step 6, the spacer, or containing device, is removed and the blank is ready for subsequent manufacturing operations.

Referring to FIG. 6, methods of coupling the hard section of the contact lens to the soft section will now be described. Conventional hybrid contact lenses are generally not durable, in part because of the weak chemical bonding between the hard and soft sections of the lens. One feature of the present invention is that a variety of coupling configurations are contemplated that securely couple the hard and soft sections of a hybrid contact lens.

One embodiment of the present invention employs an angled, or sloped surface between the hard and soft contact lens sections, thereby increasing the surface area, and thus the bonding force, or strength between the two sections. Other embodiments use a variety of different surface features, or surface geometries that increase the durability and comfort of a hybrid contact lens.

For example, the bonding angle 50, shown in FIG. 6, may vary from almost O-degrees to almost 90 degrees. That is, if a contact lens constructed according to the present invention was pressed against a flat surface, the angle defined by the interface between the hard and soft sections of the lens could vary from almost parallel to the flat surface to almost perpendicular to the flat surface.

In addition, the interface between the hard and soft sections of the contact lens may include a variety of surface configurations, or geometries 55. As shown in FIG. 6, these surface geometries 55 may include ledges, protuberances, or substantially V- or W-shaped projections. Other surface geometries 55 may include serrations, gradations, or any other shape that is not substantially straight, or planar.

Referring now to FIG. 6A, a preferred hard-soft lens bonding method is illustrated. In this embodiment of the present invention, increasing the surface area between the rigid and soft lens components increases bonding strength between the two materials and minimizes lens breakage, or failure. Another advantage of this embodiment is that it provides a smooth transition between the rigid or hard, and soft materials. This produces an exceptionally comfortable lens.

As shown in FIG. 6A, an interface, or junction 75 between the hard, or substantially rigid lens material 65, and the soft lens material 70 is illustrated. Also shown is angle “A” that may range between about 95 degrees to about 170 degrees. In a preferred embodiment, angle A ranges between about 110 degrees to about 165 degrees. As illustrated, the interface between the hard, or substantially rigid lens material 65, and the soft lens material 70 is substantially V-shaped. Put differently, the interface comprises two intersecting planes that meet within the lens. This lens junction configuration provides a safety feature in the unlikely case of lens material separation during wear. Because of the V-shape, the edge of the hard lens material 65 is not “blade” shaped, and thus a sharp edge will not contact the cornea or eyelid, eliminating the risk of cuts, or abrasions.

The hard and soft sections of a contact lens constructed according to the present invention may be joined, or coupled by a bonding material or resin comprised of the following monomer mixtures or their derivatives: vinyl acetate; trifluoroethanol; methyl methacrylate; ethylene diamine; 2-hydroxyethyl methacrylate (HEMA) and other esters of methacrylic acid formulated from acrylic bases with fluorinated alkyl or aryl, silicone, styrene moiety in the structure and resultant polymers such as polystyrene; fluorine/styrene; and silicone/styrene.

The soft section of the contact lens constructed according to the present invention may be comprised of a variety of materials. These materials may include the following monomer mixtures or their derivatives: poly HEMA; hydroxyethyl acrylate; dihydroxypropyl methacrylate; polyethylaneglycol; acetoxysilane; (trimethylsiloxyethyl)methacrylate; trimethylesiloxy; ethyleneglycol-dimethacrylate; phenylethyl acrylate; and polyethylene oxide. It will be appreciated to those skilled in the art that other types of materials may be employed.

Hybrid Contact Lens Surface Treatments

One feature of the present invention is that a variety of contact lens surface treatments are contemplated. These surface treatments may be added, for example, for the purpose of improving the comfort of the lens by means of improving the in-vivo wetting of the lens material. Another reason for using surface treatments is to create a uniform pre-lens tear film thickness. Variations in pre-lens tear film thickness induce aberrations while a uniform pre-lens tear film thickness allows the other aberration corrections to reach full effectiveness.

One embodiment of a hybrid contact lens constructed according to the present invention may include a surface treatment that provides uniform pre-lens tear film thickness between normal blinking action. These treatments may comprise one or more of the following embodiments: 1) Plasma—the lens is placed in the presence of gases that are modified by oscillating electromagnetic energy. This creates a surface oxidation that generate functional groups such as OH or NH on the lens surface, which make the lens surface more wettable; 2) Ionic surfactants—polar molecules are presented to the ionic lens surfaces with a resultant bonding of the molecules to the surface. An example is sodium dodecyl sulfide. The 12-carbon chain combined with lauryl sulfonic acid provides a substrate that supports a more uniform tear film thickness; 3) Non-ionic surfactants—The lens may be exposed to non-ionic surfactants that provide a film on the lens. An example is an ethylene glycol chain; 4) Soluble polymers—films of soluble polymers can be applied to the rigid gas permeable material after manufacturing. Examples are TEFLON, N,N-dimethyacrylamide and HEMA. Other types of surface treatments are also contemplated.

Methods of Prescribing and Fitting a Hybrid Contact Lens

The present invention also contemplates methods of prescribing and fitting a hybrid contact lens. One method relates to non-rotating lenses for correcting high order aberrations that include methods of placing the coordinates of the aberration measurement over the coordinates of the pupil. Another comprises methods of placing a multifocal over the coordinates of the pupil and customizing the design of the multifocal with measurements of high order aberrations and pupil size.

One method of prescribing and fitting a hybrid contact lens employs a set of precision hybrid lenses with either spherical, aspherical or toroidal posterior surfaces and spherical, aspherical or toroidal anterior surfaces. For a final monofocal lens, one embodiment contains a posterior aspherical surface and an anterior spherical surface. For a final multifocal lens one embodiment contains a posterior aspherical surface and an anterior aspherical surface.

One prescribing method of the present invention employs a central registration mark or marks concentric with the lens geometric center that are placed on either the anterior or posterior surfaces or within the matrix of either the rigid central portion, the intermediate adhesion enhancement zone or in the soft portion of a contact lens. In the preferred embodiment the rigid portion is at least 9 mm in diameter and a minimum of three, marks are placed at a chord diameter of about 8 mm. In the preferred embodiment the diameter of the overall lens is approximately 14.0 mm.

A contact lens from the set with a posterior rigid surface that approximates the sagittal depth of the respective eye over the chord diameter of the rigid portion is placed on the eye and allowed to equilibrate. The degree of rotational and translational movement is observed. In the preferred embodiment the movement observed should be less than 5 degrees rotational and 0.3 mm translational. Upon determination that the movement meets the required limit the residual high and low order aberrations are measured through the lens along with the relative coordinates of the lens marks and the pupil margin, limbal margin or other anatomical features. In the preferred embodiment an instrument having the capability of detecting the lens marks and the pupil margin along with the residual high and low order aberrations is used.

An alternative embodiment of the present invention may include infrared-responsive marks, such as one or more registration marks, one or more concentric marks, or other suitable marks, which emit or reflect infrared light. For example, some types of wavefront aberrometers employ infrared light, which is generally in the form of a laser. During examination of an eye fitted with a hybrid hard-soft contact lens constructed according to the present invention, the infrared-reflecting marks in the hybrid lens will be easily visible, enabling simultaneous evaluation of registration error, as well as aberrations. In one embodiment, indocyan dye that fluoresces when exposed to ultraviolet light is employed, but it will be appreciated that, other dyes, powders, or other types of ultraviolet and infrared-responsive products may be employed.

Another method of prescribing and fitting a hybrid contact lens employs a set of precision rotating and non rotating hybrid contact lenses having known ocular surface profiles, optical corrections and thickness profiles. In one embodiment, the lenses contain circumferential marks in the mid periphery. A lens is selected and applied to the eye and allowed to equilibrate. The coordinates of the marks and the pupil are determined. The aberrations of the lens-eye system are measured. A mathematical model provides analysis of the known thickness profile, the registration error of the coordinates of the lens and the pupil, and the residual lens-eye aberrations to derive the computer numerically controlled lathe files for diamond turning a resultant thickness profile for a final contact lens having the same ocular surface profile.

For example, one prescribing and fitting method of the present invention may include the steps of: selecting the initial lens to conform to the shape of the underlying cornea; capturing an image of the circumferential marks and the pupil margin; measuring the residual low and high order aberrations of the lens-eye system; performing analysis utilizing the known ocular surface profile of the lens, the initial lens thickness profile, the registration error, and the residual lens-eye aberration error to determine the resultant files for generating a final contact lens.

Another method of prescribing and fitting a hybrid contact lens employs a set of contact lenses having a known central zone ocular surface geometry, thickness, anterior surface geometry and diameter. The preferred residual lens eye aberration correction and coordinate disparity are determined by clinical measurement, and the thickness profile variation is derived by computer modeling, or other methods, in order to specify a superiorly performing lens.

Yet another method of prescribing and fitting a hybrid contact lens employs a set of contact lenses with fixed ocular surface geometries, overall diameters and front surface geometries, over which clinical measurements are made from which the final prescription parameters are derived by computation, or other methods.

Another method of the present invention comprises correcting visual acuity deficiencies in presbyopia by reduction of the residual lens-eye aberrations. The method uses a set of hybrid contact lenses having a known ocular surface profile and thickness profile and containing circumferential marks for the purpose of registration of the final optical correction with the coordinates of the optical system of the eye. The method steps may include: selecting the initial lens to conform to the shape of the underlying cornea; capturing an image of the circumferential marks and the pupil margin; measuring the size of the pupil in photopic, mesopic and/or scotopic illumination; measuring the residual low and high order aberrations of the lens-eye system; and performing analysis utilizing the known ocular surface profile, the initial lens thickness profile, the registration error, the pupil size and the residual lens-eye aberration error to determine prescription information for generating a final contact lens. In one embodiment of this method, the diameter of the near focused optical correction may be in the range of about 1.8 mm to about 4.0 mm.

Another method of the present invention employs a multifocal contact lens and corrects visual acuity deficiencies in presbyopia by reduction of the residual lens-eye aberrations. The method uses a set of multifocal hybrid contact lenses having a known ocular surface profile and thickness profile and containing circumferential marks for the purpose of registration of the final optical correction with the coordinates of the optical system of the eye. The method steps may include: selecting the initial lens to conform to the shape of the underlying cornea having a multifocal anterior surface; capturing an image of the circumferential marks and the pupil margin; measuring the size of the pupil in photopic, mesopic and/or scotopic illumination; measuring the residual low and high order aberrations of the lens-eye system; and performing analysis utilizing the known ocular surface profile, the initial lens thickness profile, the registration error, the pupil size and the residual lens-eye aberration error to determine prescription information for generating a final multifocal contact lens. In one embodiment of this method, the diameter of the near focused optical correction may be in the range of about 1.8 mm to about 4.0 mm.

Another method of the present invention employs a multifocal contact lens and corrects visual acuity deficiencies in presbyopia by reduction of the residual lens-eye aberrations. This method also incorporates information relating to a light transmittance pattern. The method uses a set of multifocal hybrid contact lenses having a known ocular surface profile and thickness profile, light transmittance pattern, and containing circumferential marks for the purpose of registration of the final optical correction with the coordinates of the optical system of the eye. The method steps may include: selecting the initial lens to conform to the shape of the underlying cornea having a multifocal anterior surface; capturing an image of the circumferential marks and the pupil margin; measuring the size of the pupil in photopic, mesopic and/or scotopic illumination; measuring the residual low and high order aberrations of the lens-eye system; and performing analysis utilizing the known ocular surface profile, the initial lens thickness profile, the registration error, the light transmittance pattern, the pupil size and the residual lens-eye aberration error to determine prescription information for generating a final multifocal contact lens. In one embodiment of this method, the diameter of the near focused optical correction may be in the range of about 1.8-mm to about 4.0 mm.

The above-described methods of prescribing and/or fitting a hybrid contact lens may also employ additional method steps or additional devices. For example: the method of determining the difference in the coordinates of the center of the circumferential lens marks and the pupil margin may incorporate a reticle of a biomicroscope or a camera with subsequent manual or electronic digital image detection. In addition, the method of measuring the residual aberrations of the lens-eye system may incorporate Shack-Hartmann aberrometry, aberrometers utilizing Tscherning technology, laser ray-tracing, holographic grid or Talbot interferometry technology.

Correction for Various Components of the Visible Light Spectrum

Aberrometry performed with the contact lens in place provides us with knowledge of the angles that the rays emerging from the anterior lens make with respect to the visual axis. In the perfect case, the rays would all emerge parallel to the visual axis. But as illustrated in FIG. 7, in the presence of aberrations these rays make an angle with respect to the visual axis and this angle is not restricted to the plane of the paper. To correct these aberrations, there are generally two variables to modulate. The first variable is the slope of the contact lens at the point each ray emerges from the contact lens. Changing this slope will change the direction of the ray exiting the eye via Snell's Law. There will exist a slope of the anterior or posterior contact lens surface that causes the ray to exit parallel to the visual axis. The second variable is the local lens thickness at the point where each ray exits the contact lens. As this thickness is adjusted, the slope of one or both of the surfaces for the path of the ray at this point also needs to change in order to keep the emerging ray parallel to the visual axis. There will exist a set of local thicknesses and slopes that simultaneously cause all of the emerging rays to be parallel to the visual axis and keep the overall thickness of the lens reasonable, that is, not too thin or too thick.

Aberrometry is normally only performed at one wavelength, usually in the infrared. However, as illustrated in FIG. 8, the slopes of the various rays will depend on the color of the light. In general, blue lights rays will be more convergent than the green light rays. The red light rays will be more divergent than the green light rays.

The dilemma now is which color rays should be made parallel to the visual axis. If the eye responded equally to all colors in the visible range (wavelengths of about 380 nanometers (nm) to about 780 nm), you would make the rays that corresponded to the middle wavelength parallel to the visual axis. In this manner, half of the light would be diverging and half of the light would be converging as it left the eye.

Referring to FIG. 9, for a uniform response, the center wavelength of the visible spectrum would be ideal for correcting aberrations since, the equal areas of the rectangles on either side of this wavelength means equal amounts of energy is distributed around this wavelength.

However, the eye does not respond to all wavelengths the same. The photopic response curve, illustrated in FIG. 10, shows that the eye is more sensitive to the red/green end of the spectrum. The same sort of concept as described above can now be used to determine the ideal wavelength for correcting aberrations. The ideal wavelength gives equal areas under the photopic response curve on either side, as shown in FIG. 10.

In addition to the variation in response of the eye to different colors, the present invention may also vary the transmission of the contact lens to different colors. This may be beneficial to reducing the effects of chromatic aberration in the eye. If the contact lens transmission is multiplied by the photopic response of the eye, a net response of the eye results, as illustrated in FIG. 11. One ideal wavelength is based on this net response which again gives equal areas under the curve. This ideal wavelength is then used as the target for correcting aberrations by the means described above.

For example, for either a final monofocal or multifocal lens, one embodiment hybrid contact lens constructed according to the present invention contains colorants that reduce the transmission at both the blue and red end of the visible spectrum thereby narrowing the band of transmitted light and potentially shifting the peak of the transmission curve of the lens. A contact lens of the present invention may therefore include color additives for the purpose of reducing light transmission, or color additives for the purpose of reducing chromatic aberration.

An alternative examples utilizes a calculation based on the known bandwidth of a pre-existing lens material and the output of the monochromatic aberrometry measurement to determine the optimum lens thickness profile.

Methods of Manufacturing a Hybrid Contact Lens by Chemical Bonding

The present invention discloses a hybrid contact lens that provides clear vision, while featuring high gas permeability for enhanced comfort. Methods of manufacturing such a hybrid contact lens are described herein with respect to FIGS. 1-6. In accordance with the principles of the present invention, methods of manufacturing a hybrid contact lens by chemical bonding will now be described with respect to FIGS. 12-29. More particularly, the methods pertain to chemically bonding a substantially flexible hydro-gel soft skirt portion to a substantially rigid high DK gas permeable core center portion.

Suitable materials for the substantially flexible portion include, but are not limited to: hydroxyethylmethacrylate (HEMA); methyl methacrylate (MMA); Ethyl methacylate (EMA); aminoaklyl containing acrylate or methacrylate; N-vinyl pyrrolidone (NVP); 2-methoxyethyl methacrylate (MEMA); ethylene glycol methacrylate (EGMA); trifluoropropyl methacrylate; pentafluoropentyl methacylate; N,N-dimethylacrylamide (DMA); acrylamide; methacylamide; tetramethyldisiloxane ethylene glycol dimethacrylate; perfluorophenyl methacrylate; 2-(trimethylsiloxyl)ethyl methacrylate; N-fluoroalkyl methacylamide; bis(2-methacryloxyphenyl)propane; (N,N-dimethylamino-ethyl)methacrylate; and combinations of any of these monomers and/or silicone hydrogel formulations such Cibavision lotrafilcon. As would be understood to those of ordinary skill in the art, the above list is by no means exhaustive as other soft skirt materials may be employed as the substantially flexible portion without departing from the scope of the present invention.

Suitable materials for the substantially rigid portion include, but are not limited to: fluorosilicone acrylate; siliconated, styrene; fluoroacrylate; fluorometharylate, perfluorianted acrylate and methacrylate; any high DK or Hyper DK gas permeable rigid contact lens bottoins with DK of 70 (ISO), such as Boston 7 Envision, Boston EO, Boston Equales, Boston Equalens 2, Boston XO, Fluoroperm 151, Fluoroperm 92, Fluoroperm 92, Fluoro 700, Menicon SE-P, Menicon Z; any other high DK materials; and any combination of these materials. Of course, as would be understood to those of ordinary skill in the art, this list is by no means exhaustive as other materials may be employed as the substantially rigid portion without departing from the scope of the present invention.

A method of manufacturing a hybrid contact lens using a molded cup will now be described with respect to FIGS. 12-15. Referring to FIG. 12, molded cup 100 comprises horizontal surface 102, a cylindrical outer wall 104 disposed substantially normal to horizontal surface 102 and a cylindrical inner wall 106. The area within inner wall 106 comprises a cylindrical inner section 109 for receiving substantially rigid material, and the area between the inner and outer walls comprises a cylindrical outer section 111 for receiving substantially flexible material.

Inner wall 106 preferably comprises a pre-form optical grade divider that divides the substantially rigid inner portion and the substantially flexible outer portion. In addition, inner wall 106 preferably is bondable with both rigid and flexible materials used to form the contact lens. Suitable materials for the molded cup include, but are not limited to, polypropylene, polyethylene, polyethylene terephthalate (PET), polycarbonate and optical grade plastics. The inner and outer walls optionally are coated with an adhesive to promote bonding with the flexible and rigid portions.

Preferably, the molded cup remains part of the finished contact lens. Alternatively, portions of the molded cup may be removed during the casting process. For example, inner wall 106 may be removed after pouring and curing the substantially rigid portion, and outer wall 104 may be removed after pouring and curing the substantially flexible portion. According to some embodiments, molded cup 100 further comprises a lower cylinder 108 that forms lower section 113, which is dimensioned to produce a gripping area that conforms to the collet of a computer numerically controlled lathe or other machining apparatus. In these embodiments, horizontal surface 102 preferably includes a central opening 110 such that lower section 113 may be filled during manufacturing. Alternatively, lower section 113 may be pre-filled before manufacturing. According to other embodiments, lower cylinder 108 is not provided.

In the illustrated embodiment, inner wall 106 or divider 106 is disposed at an angle A with respect to horizontal surface 102. Angle A may be any angle from about 5 degrees to about 175 degrees, but preferably is selected to maximize the bonding strength between the rigid and flexible portions of the contact lens. Inner wall 106 optionally includes a bend B adapted to further increase the bonding strength between the rigid and flexible portions. As would be understood to those of ordinary skill in the art, many alternative inner wall configurations may be employed without departing from the scope of the present invention. For example, examples of alternative bonding angles between the flexible and rigid portions are described above with respect to FIGS. 6 and 6A. Additionally, examples of alternative inner wall configurations will now be described.

Referring to FIG. 13A, molded cup 100 includes an alternative inner wall 114 that is disposed substantially normal to horizontal surface 102 (i.e., angle A is about 90 degrees). In addition, inner wall 114 does not include a bend. Referring to FIG. 13B, molded cup 100 includes an alternative inner wall 116 that is disposed at an acute angle with respect to horizontal surface 102. Referring to FIG. 13C, molded cup 100 includes an alternative inner wall 118 that is disposed at an obtuse angle with respect to horizontal surface 102. Referring to FIG. 13D, molded cup 100 includes an alternative inner wall 120 including a plurality of bends B. Bends B preferably increase the bonding strength between the rigid and flexible portions. Additionally, inner wall 120 is disposed at an angle A with respect to horizontal surface 102. Similar to the embodiment disclosed above with respect to FIG. 12, angle A may be any angle from about 5 degrees to about 175 degrees, but preferably is selected to maximize the bonding strength between the rigid and flexible portions of the contact lens.

Referring to FIG. 14, a predetermined amount of liquefied resin of substantially rigid material is poured within inner section 109 such that the material: (1) fills lower section 113 via opening 110, thereby forming gripping area 128; and (2) substantially fills inner section 109, thereby forming substantially rigid portion 126. Then, the molded cup is placed into a programmed curing environment and the rigid material is cured with heat, UV light, or a combination of both.

Alternatively, a predetermined amount of liquefied resin of substantially rigid material is poured within inner section 109 such that the material only fills lower section 113, thereby forming gripping area 128. Then, the molded cup is placed into a programmed curing environment and the rigid material is cured with heat, UV light, or a combination of both. After curing, an additional predetermined amount of liquefied resin of rigid material is poured within inner section 109 such that the additional material substantially fills inner section 109, thereby forming substantially rigid portion 126. Then, the molded cup is again placed into the programmed curing environment and the rigid material is cured with heat, UV light, or a combination of both.

Referring to FIG. 15, after curing the substantially rigid material, a predetermined amount of liquefied resin of substantially flexible material is poured into outer section 111, thereby forming substantially flexible portion 130. Then, the molded cup is again placed into the programmed curing environment and the flexible material is cured with heat, UV light, or a combination of both. After curing the flexible material, the lens is ready to be lathed, or otherwise machined, into a finished, fracture-resistant hybrid contact lens.

A method of manufacturing a hybrid contact lens using a block mold will now be described with respect to FIGS. 16-21. Referring to FIG. 16, block mold 134 comprises a pair of halves 136, 138 that are attached along a breaking plane 140. Block mold halves 136, 138 preferably are symmetric about breaking plane 140. Block mold 134 further comprises a central void 144, 146 that defines an upper section 144 and a lower section 146. Central void 144, 146 forms an opening 150 in a substantially horizontal top surface 152 of block mold 134 such that the upper and lower sections may be filled with liquefied resin of the rigid material to form the hard portion of the contact lens.

According to some embodiments, lower section 146 preferably is dimensioned to produce a gripping area that conforms to the collet of a computer numerically controlled lathe or other machining apparatus. In these embodiments, an opening 148 exists between the upper and lower sections such that lower section 146 may be filled with liquefied resin during manufacturing. According to other embodiments, lower section 146 is not provided.

Upper section 144 includes an outer wall 156 formed by an inside surface of the block mold halves. Outer wall 156 forms the shape of the junction between the rigid and flexible portions of the contact lens. In the illustrated embodiment, outer wall 156 is disposed at an angle A with respect to top surface 152. Angle A may be any angle from about 5 degrees to about 175 degrees, but preferably is selected to maximize the bonding strength between the rigid and flexible portions of the contact lens. Outer wall 156 optionally includes a bend B adapted to further increase the bonding strength between the rigid and flexible portions. As would be understood to those of ordinary skill in the art, many alternative outer wall configurations may be employed without departing from the scope of the present invention. Some of these alternative outer wall configurations will now be described.

Referring to FIG. 17A, upper section 144 of the central void includes an alternative outer wall 158 that is disposed substantially normal to horizontal surface 152 (i.e., angle A is about 90 degrees). In addition, outer wall 158 does not include a bend. Referring to FIG. 17B, upper section 144 includes an alternative outer wall 160 that is disposed at an acute angle with respect to horizontal surface 152. Referring to FIG. 17C, upper section 144 includes an alternative outer wall 162 that is disposed at an obtuse angle with respect to horizontal surface 152. Referring to FIG. 17D, upper section 144 includes an alternative inner wall 164 including a plurality of bends B. Bends B preferably increase the bonding strength between the rigid and flexible portions of the contact lens.

Referring to FIG. 18, a predetermined amount of liquefied resin of substantially rigid material is poured into opening 150 such that the material: (1) fills the area within lower section 146, thereby forming gripping area 172; and (2) substantially fills upper section 144, thereby forming substantially rigid section 170. Then, the block mold is placed into a programmed curing environment and the rigid material is cured with heat, UV light, or a combination of both. Alternatively, a predetermined amount of liquefied resin of substantially rigid material is poured into opening 150 such that the material only fills the area within lower section 146, thereby forming gripping area 172. Then, the block mold is placed into a programmed curing environment and the substantially rigid material is cured with heat, UV light, or a combination of both. After curing, an additional predetermined amount of liquefied resin of rigid material is poured into opening 150 to substantially fill upper section 144, thereby forming substantially rigid section 170. Then, the block mold is again placed into the programmed curing environment and the rigid material is cured with heat, UV light, or a combination of both.

Referring to FIG. 19, after curing the substantially rigid material, block mold 134 is broken along breaking plane 140 and the cured section of rigid material (comprising rigid section 170 and gripping area 172) is removed from the block mold halves. At this point, the surface of the cured section of rigid material optionally is primed or coated for better bonding. Referring to FIG. 20, a guard 178, 180 comprising a substantially horizontal section 178 and a cylindrical sidewall 180 is attached on top of gripping area 172 using a suitable adhesive. Referring to FIG. 21, a predetermined amount of liquefied resin of flexible material is then poured into the area between rigid section 170 and sidewall 180, thereby forming substantially flexible portion 182.

With further reference to FIG. 21, the materials are then placed into the programmed curing environment and the substantially flexible material is cured with heat, UV light, or a combination of both. The hybrid materials (i.e., rigid section 170 and flexible section 182) are now primed to be lathed, or otherwise machined, into a finished, fracture-resistant hybrid contact lens. Unlike the embodiment disclosed with respect to FIGS. 12-15, there is no wall or divider disposed between the rigid and flexible portions.

A method of manufacturing a hybrid contact lens using a base curve mold will now be described with respect to FIGS. 22-24. Referring to FIG. 22, base curve mold assembly 190 comprises base curve mold 192, inner wall 194 or divider 194, outer wall 196 disposed around the outer circumference of base curve mold 192. Optionally, one or more centering webs 198 are provided between the inner and outer walls to ensure proper positioning of inner wall 194 with respect to a vertically disposed base plane 200 that passes through the center of base curve mold 192. Inner wall 194 acts as a separator and junction surface between the rigid and flexible materials. Inner wall 194 preferably is a pre-form optical grade divider that is bondable with both rigid and flexible materials used to form the contact lens. According to some embodiments, inner wall 194 is coated with an adhesive to promote bonding with the rigid and flexible portions.

In the illustrated embodiment, inner wall 194 is substantially vertically disposed (i.e., parallel to plane 200). However, similar to the embodiments described above with respect to FIGS. 12-21, inner wall 194 may be disposed at any angle from about 5 degrees to about 175 degrees with respect to a horizontal plane. Through the process of trial and error an angle may be chosen that maximizes bonding strength between the rigid and flexible portions of the contact lens. Inner wall 194 optionally includes one or more bends B adapted to further increase the bonding strength. Of course, as would be understood to those of ordinary skill in the art, many alternative inner wall configurations may be employed without departing from the scope of the present invention.

Referring to FIG. 23, a predetermined amount of liquefied resin of substantially rigid material is poured within inner wall 194 to fill the area therebetween, thereby forming substantially rigid portion 202. Then, the base curve mold assembly is placed into a programmed curing environment and the rigid material is cured with heat, UV light, or a combination of both. Referring to FIG. 24, after curing the rigid material, a predetermined amount of liquefied resin of substantially flexible material is poured into the area between inner wall 194 and outer wall 196, thereby forming substantially flexible portion 204. Then, the base curve mold assembly 190 is again placed into the programmed curing environment and the flexible material is cured with heat, UV light, or a combination of both. After curing the flexible material, the outer wall and centering webs are removed and the anterior surface of the lens is ready to be lathed, or otherwise finished.

A method of manufacturing a hybrid contact lens using a base curve block mold assembly will now be described with respect to FIGS. 25-29. Referring to FIG. 25, base curve block mold assembly 210 comprises base curve mold 212 and a pair of block mold halves 214, 216 that are symmetrically disposed about a vertical plane 218 passing through the center of base curve mold 212. Base curve block mold assembly 210 further comprises a central void 222 disposed in the area above base curve mold 212 between block mold halves 214, 216. Central void 222 is adapted to be filled with liquefied resin of the rigid material to form the hard portion of the contact lens.

Central void 222 includes an outer wall 226 formed by an inside surface of the block mold halves. Outer wall 226 forms the shape of the junction between the rigid and flexible portions of the contact lens. In the illustrated embodiment, outer wall 226 is disposed substantially parallel to vertical plane 218; However, similar to the embodiments described above with respect to FIGS. 12-24, outer wall 226 may be disposed at any angle from about 5 degrees to about 175 degrees with respect to a horizontal plane. Through the process of trial and error an angle may be chosen that maximizes bonding strength between the rigid and flexible portions of the contact lens. Additionally, outer wall 226 optionally includes one or more bends B adapted to further increase the bonding strength. Of course, as would be understood to those of ordinary skill in the art, many alternative outer wall configurations may be employed without departing from the scope of the present invention.

Referring to FIG. 26, a predetermined amount of liquefied resin of substantially rigid material is poured into central void 222 such that the material fills the area within central void 222, thereby forming substantially rigid section 230. Then, the block mold is placed into a programmed curing environment and the rigid material is cured with heat, UV light, or a combination of both. Referring to FIG. 27, after curing the rigid material, block mold halves 214, 216 are separated and removed from base curve mold 212. Referring to FIG. 28, a curvilinear sidewall 234 is attached around the perimeter of base curve mold 212 using a suitable adhesive.

Referring to FIG. 29, a predetermined amount of liquefied resin of substantially flexible material is then poured into the area between rigid section 230 and sidewall 234, thereby forming substantially flexible portion 236. The materials are then placed into the programmed curing environment and the flexible material is cured with heat, UV light, or a combination of both. After curing the flexible material, the sidewall is removed and the anterior surface is lathed, or otherwise finished.

A method of manufacturing a hybrid contact lens using a using a pre-shape mold assembly including a pre-machined substantially rigid center portion as a molded insert of a soft-skirt mold will now be described with respect to FIGS. 30-33. Referring to FIG. 30, substantially rigid center portion 250 is formed and cured before being placed in the mold assembly. According to some embodiments, the rigid center portion is pre-coated or pre-treated with an adhesive to promote bonding with the flexible outer portion. Referring to FIG. 31, pre-shape mold assembly 252 comprises a base curve mold 254 and a pair of block mold halves 256, 258 that are symmetrically disposed about a vertical plane 260 passing through the center of base curve mold 254.

Pre-shape mold assembly 252 further comprises a substantially bowl-shaped void 264 disposed between the base curve mold and the block mold halves. Bowl-shaped void 270, 272 comprises an inner portion 270 for receiving substantially rigid center portion 250 and an outer portion 272 that is filled with a substantially flexible material. In addition, pre-shape mold assembly 252 preferably includes a central void 266 disposed in the area above base curve mold 254 between block mold halves 256, 258. Central void 266 is dimensioned to permit the substantially rigid center portion to be inserted into inner portion 270 after it is formed and cured. One or more injection apertures 274 preferably are provided in the pre-shape mold assembly for filling the outer portion of bowl-shaped void 270, 272.

Referring to FIG. 32, a predetermined amount of liquefied resin of substantially rigid material is injection into outer portion 270, thereby forming substantially flexible outer portion 276. Then, pre-shape mold assembly 252 is placed into a programmed curing environment and the flexible material is cured with heat, WV light, or a combination of both. Referring to FIG. 33, after curing the flexible material, the mold is separated and the finished contact lens is removed from the mold. According to some embodiments, the contact lens may require machining of the anterior or posterior surfaces before it is ready for use.

As disclosed above with respect to FIG. 6, the bonding angle between the flexible and rigid portions of the contact lens may vary from almost 0 degrees to almost 90 degrees. In addition, the interface between the flexible and rigid portions may include a variety of surface configurations, including, but not limited to, ledges, protuberances, substantially V- or W-shaped projections, serrations, gradations, and any other shape that is not substantially straight, or planar. Alternatively, as disclosed above with respect to FIG. 6A, a junction may be provided between flexible and rigid portions.

With further reference to FIGS. 30-33, the substantially rigid portion may comprise one or more of the following monomers, monomer mixtures, and their derivatives: trimeththyl-siloxyl; methyl-methacrylate; ethyl-methacrylate; ethylene glycol di-methacrylate; octafluoro pentyl-methacrylate; tetra-methyldisiloxane; ethylene glycol di-methacrylate; pentafluoro phenylacrylate; 2-(trimethylsiloxyl) methacrylate; bis(2-metharyloxyphenyl) propane; N-[2-(N,N-dimethylamino)ethyl]; onethacrylate; N-[2-(n,n-dimethylamino)ethy]; methacryalte; vinyl-pyrolidone; N,N-dimathacrylamide; acrylamine; hydroxyethyl methacrylate; siloxane ethylene glycol di-methacrylate; trifluoroethyl methacrylate; pentafluorostyrene; pentafluoropropyl methacrylate; unsaturated polyester; p-vinyl benzyl hexafluoroisopropyl ether; siloxanylalkylamide; and combinations thereof. As would be understood to those of ordinary skill in the art, many other materials may be used to form the substantially rigid portion without departing from the scope of the present invention.

For the embodiment disclosed with respect to FIGS. 30-33, the substantially flexible portion may comprise one or more of the following monomer mixtures and their derivatives: poly HEMA; hydroxyethyl acrylate; dihydroxypropyl methacrylate; polyethylaneglycol; acetoxysilane; trimethylesiloxy; ethyleneglycol-dimethacrylate; phenylethyl acrylate; zero-gel; Silicon-Hydrogel; polyethylene oxide; and combinations thereof. As would be understood to those of ordinary skill in the art, many other materials may be used to form the substantially flexible portion without departing from the scope of the present invention.

For the embodiment disclosed with respect to FIGS. 30-33, the pre-treat or pre-coat between flexible and rigid portions of the contact lens may comprise an adhesive or resin on or more of the following monomer mixtures and their derivatives: vinylacetate; trifluoroethanol; methacrylate; ethanediamine; 2-hydroxyethylmethacrylate (HEMA) and other esters of methacrylic acid formulated from acrylic bases; fluorine; silicone; fluorine/silicone; styrene and resultant polymers such as polystyrene; fluorine/styrene; silicone/styrene; and combinations thereof. As would be understood to those of ordinary skill in the art, many other materials may be used to form pre-treat or pre-coat without departing from the scope of the present invention.

Further methods of manufacturing a hybrid contact lens according to the present invention involve pouring the rigid and flexible materials in the reverse order such that the flexible material is poured and cured before the rigid material. For the block mold embodiments, this will require the creation of blocks that fill the central void such that the outer, flexible portion may be poured and cured first. Additional methods involve pouring both rigid and flexible materials at substantially the same time, then curing the materials simultaneously.

Additional methods of manufacturing a hybrid contact lens according to the present invention involve molding or lathing a standard base curve mold with a standard or semi-customized front surface, then using a thermal or laser energy to modify the refractive index of the center material to a desired optical requirement. Advantageously, these methods replace expensive custom lathing and molding operations. Further methods involve molding both the posterior and anterior surfaces of the contact lens. Other methods involve the application of a mechanical force or thermal molding.

Alternative manufacturing methods of the present invention may include: molding of the posterior surface and diamond turning of the molded blank; contour cutting of the anterior surface of a posterior curve finished blank; etching the anterior or posterior surface of a posterior curve finished blank or predicate lens anterior or posterior surface; thin film deposition of a predicate lens anterior or posterior surface; and laser ablation of a predicate lens anterior or posterior surface.

Thus, it is seen that a hybrid hard-soft contact lens system, method, method of manufacture and article of manufacture is provided. One skilled in the art will appreciate that the present invention can be practiced by other than the above-described embodiments, which are presented in this description for purposes of illustration and not of limitation. The description and examples set forth in this specification and associated drawings only set forth preferred embodiment(s) of the present invention. The specification and drawings are not intended to limit the exclusionary scope of this patent document. It is noted that various equivalents for the particular embodiments discussed in this description may practice the invention as well. 

1-55. (canceled)
 56. A method of manufacturing a hybrid contact lens, comprising the steps of: providing a block mold including a central void; pouring liquefied resin of a substantially rigid material within the central void; curing the substantially rigid material; removing the substantially rigid material from the block mold; attaching a guard to the substantially rigid material; pouring a predetermined amount of liquefied resin of flexible material into an area between the substantially rigid section and the guard; and curing the substantially flexible material.
 57. The method of claim 56, wherein the central void includes an upper section including an outer wall formed by an inside surface of the block mold halves.
 58. The method of claim 57, wherein the outer wall forms the shape of the junction between the substantially rigid material and the substantially material.
 59. The method of claim 56, wherein the outer wall is disposed at an angle with respect to a horizontal surface.
 60. The method of claim 59, wherein the angle is between 5 and
 175. 61. The method of claim 59, wherein the angle is selected to maximize the bonding strength between the rigid and flexible portions of the contact lens.
 62. The method of claim 59, wherein the angle is about 90 degrees.
 63. The method of claim 59, wherein the angle is acute.
 64. The method of claim 59, wherein the angle is obtuse.
 65. The method of claim 58, wherein the outer wall includes one or more bends for increasing the bonding strength between the rigid and flexible portions.
 66. The method of claim 57, wherein the central void further comprises a lower section.
 67. The method of claim 66, wherein the step of pouring liquefied resin of the substantially rigid material within the central void includes the step of pouring liquefied resin of the substantially rigid material within the lower section.
 68. The method of claim 66, wherein the lower section is dimensioned to produce a gripping area that conforms to the collet of a computer numerically controlled lathe or other machining apparatus.
 69. The method of claim 56, wherein the curing steps involve the application of heat, UV light, or a combination of both heat and UV light.
 70. The method of claim 56, wherein the step of removing the substantially rigid material from the block mold includes the step of breaking the block mold along a breaking plane.
 71. The method of claim 56, further comprising the step of removing the guard after curing the substantially flexible material.
 72. The method of claim 56, wherein the guard includes a horizontal lower surface and a cylindrical sidewall.
 73. The method of claim 56 wherein the materials for the substantially flexible material are chosen from the group consisting of: hydroxyethylmethacrylate (HEMA); methyl methacrylate (MMA); Ethyl methacylate (EMA); aminoaklyl containing acrylate or methacrylate; N-vinyl pyrrolidone (NVP); 2-methoxyethyl methacrylate (MEMA); ethylene glycol methacrylate (EGMA); trifluoropropyl methacrylate; pentafluoropentyl methacylate; N,N-dimethylacrylamide (DMA); acrylamide; methacylamide; tetramethyldisiloxane ethylene glycol dimethacrylate; perfluorophenyl methacrylate; 2-(trimethylsiloxyl)ethyl methacrylate; N-fluoroalkyl methacylamide; bis(2-methacryloxyphenyl)-propane; (N,N-dimethylaminoethyl)methacrylate; and combinations of any of these monomers and/or silicone hydrogel formulations such Cibavision lotrafilcon.
 74. The method of claim 56 wherein the materials for the substantially rigid material are chosen from the group consisting of: fluorosilicone acrylate; siliconated, styrene; fluoroacrylate; fluorometharylate, perfluorianted acrylate and methacrylate; any high DK or Hyper DK gas permeable rigid contact lens bottoms with DK of 70 (ISO), such as Boston 7 Envision, Boston EO, Boston Equales, Boston Equalens 2, Boston XO, Fluoroperm 151, Fluoroperm 92, Fluoroperm 92, Fluoro 700, Menicon SE-P, Menicon Z; any other high DK materials; and combinations thereof.
 75. The method of claim 56, wherein the mold includes a base curve that automatically forms a posterior surface of the hybrid contact lens.
 76. The method of claim 56, further comprising the step of lathing the cured lens materials to form anterior and posterior lens surfaces.
 77. The method of claim 76, wherein surface modifications to correct aberrations of the lens-eye system are provided on the anterior and/or posterior surfaces.
 78. The method of claim 76, wherein the surface profile of the anterior and/or posterior surfaces are modified to contain a multi-focal feature for the correction of presbyopia. 